America developed no hot curing bismaleimide resin material

No American company has developed autoclave curing bismaleimide resin matrix composites. Renegade Materials recently developed a RM-3004 No autoclave (OOA) curable bismaleimide resin (BMI) prepreg. 6 hours 191 ℃ vacuum / heat-curing furnace and a separate post-curing six hours 246 ℃, display parts only 6.35 mm thick having a porosity of 0.5%. Heat and moisture cured material mechanical properties and damage tolerance and autoclave curing material quite. Wholesale masking tape

RM-3004 can be used to produce the alleged use temperature of 204? Results of C's. Verified on the plane spar parts, you can witness its good surface finish. Due to the complex shape of the spar with a tack needs and characteristics of the prepreg diaphragm, but also to maintain the carrying capacity of the main part. Renegade company designed a BMI of compatible adhesive cream product RM-3006 and RM-3007, RM-3004 for use with prepreg, RM-3000 BMI also provides a system for resin transfer molding (RTM), RM-3010 with at low pressure resin impregnation / vacuum-assisted RTM process.Masking tape